The optical, elastic anisotropic and thermodynamic properties of TiN in the NaCl (B1) structure are analyzed in
detail in the temperature range from 0 to 2000 K and the pressure range from 0 to 20 GPa. From the calculated
dielectric constants, a first order isostructural phase transition between 29 and 30 GPa is found for TiN. The absorption spectra exhibit high values ranging from the far infrared region to the ultra-violet one. The anisotropy
value of Young’s modulus of TiN is smaller than that of c-BN at 0 GPa and the anisotropy of TiN clearly increases
with an increase of pressure. The effects of pressure and temperature on the bulk modulus, Grüneisen parameter, Gibbs free energy, and Debye temperature are significant. The Grüneisen parameter of TiN is much larger
than that of c-BN. At temperatures below 1000 K, TiN’s heat capacity is much larger than that of c-BN.
Детально проаналiзовано оптичнi, пружнi анiзотропнi та термодинамiчнi властивостi TiN в структурi NaCl
(B1) в температурнiй областi вiд 0 до 2000 K i в дiапазонi тискiв вiд 0 до 20 GPa. З обчислених дiелектричних постiйних знайдено iзоструктурний фазовий перехiд першого роду мiж 29 i 30 GPa. Спектр поглинання демонструє високi значення вiд iнфрачервоної областi до ультрафiолетової. Значення анiзотропiї
модуля Юнга для TiN є менше нiж для c-BN при 0 GPa, i анiзотропiя TiN чiтко зростає з ростом тиску. Впливи тиску i температури на об’ємний модуль, параметр Грюнайзена, вiльну енергiю Гiббса i температуру
Дебая є значними. Параметр Грюнайзена для TiN є набагато бiльшим нiж для c-BN. При температурах
нижчих 1000 K, питома теплоємнiсть TiN є набагато бiльша нiж c-BN