Decoration of Carbon Nanotubes with Cerium (IV) Oxide

Abstract

Cerium (IV) oxide (ceria) nanoparticles, 6–10 nm in size, supported on carbon nanotubes (CNTs) were prepared by a chemical reaction between Ce(NO3)3 and NaOH. The effective processing parameters of ceria particles size were discussed. CNTs/CeO2 hybrids were characterized by transmission electron microscopy (TEM), selected area electron diffraction (SAED), Raman and electron paramagnetic resonance (EPR) spectroscopy. SAED and Raman spectroscopy showed that the CeO2 particles had a cubic crystal structure. EMR spectroscopy showed two paramagnetic signals related to CNTs and a third one belonging to paramagnetic defects of CeO2.

Наночастинки оксиду церію (IV) розміром 6-10 нм одержано на вуглецевих нанотрубках (ВНТ) за хімічною реакцією між Се(NО3)3 і NaOH. Встановлено ефективні параметри синтезу наночастинок оксиду церію. Нанокомпозити ВНТ/СеО2 охарактеризовано за допомогою трансмісійної електронної мікроскопії (ТЕМ), електронографії, КР- та ЕПР-спектроскопії. Методами електронографії і КР-спектроскопії виявлено кубічну кристалічну структуру СеО2. ЕПР-спектроскопія показала, що два парамагнітних сигнали мають відношення до ВНТ, а третій обумовлений парамагнітними дефектами CeO2.

Наночастицы оксида церия (IV) размером 6-10 нм получены на углеродных нанотрубках (УНТ) в результате химической реакции между Се(NО3)3 и NaOH. Установлены эффективные параметры синтеза наночастиц оксида церия. Нанокомпозиты УНТ/СеО2 охарактеризованы с помощью трансмиссионной электронной микроскопии (ТЭМ), электронографии, КР- и ЭПР-спектроскопии. Методами электронографии и КР-спектроскопии установлена кубическая кристаллическая структура CeO2. ЭПР-спектроскопия показала, что два парамагнитных сигнала имеют отношение к УНТ, а третий обусловлен парамагнитными дефектами CeO2.