IR spectra of ɣ-irradiated nanocomposites ultra-high molecular weight polyethylene / α-SiO₂

Abstract

The effect on concentration of the nanofiller α-SiO₂ filler and irradiation on the FTIR spectra of pure films polymer (ultra-high molecular weight polyethylene (UHMWPE)) and doped them this α-SiO₂ with different concentration (0, 1, 3, 5 vol.%) were investigated using FTIR technique. The samples were irradiated for different doses like 0, 50, and 100 kGy by ⁶⁰Co source with a dose rate of approximately 3.3∙10⁻³ kGy/h at room temperature. The correlation of absorption bands with occurrence of corresponding groups was carried out. The occurrence of a series of a characteristic absorptions bands of composites was shown.

З використанням FTIR-технології досліджено вплив концентрації нанодобавки α-SiO₂ і гамма-радіації на FTIR-спектри чистих полімерних (надвисокомолеклярний поліетилен (НВМПЕ)) і наповнених до різної (0, 1, 3, 5 об.%) концентрації α-SiO₂ плівок. Зразки опромінювали до доз: 0, 50 і 100 кГр джерелом ⁶⁰Co потужністю 3.3∙10⁻³ кГр/год при кімнатній температурі. Наведено співвідношення смуг поглинання знаявністю відповідних груп. Показано наявність ряду характеристичних смуг поглинання композитів.

С использованием FTIR-технологии исследовано влияние концентрации нанодобавки α-SiO₂ и гамма-радиации на FTIR-спектры чистых полимерных (сверхвысокомолекулярный полиэтилен (СВМПЭ)) и наполненных до разной (0, 1, 3, 5 об.%) концентрации α-SiO₂ пленок. Образцы облучали до доз: 0, 50 и 100 кГр источником ⁶⁰Co мощностью 3,3∙10⁻³ kГр/ч при комнатной температуре. Приведено соотношение полос поглощения с наличием соответствующих групп, а также показано наличие ряда характеристических полос поглощения композитов.