The influence of X-ray irradiation on dynamical and structural characteristics of strained NaCl crystals

Abstract

The influence of a preliminary deformation ε = 1,3% and X-ray irradiation to exposure doses 0…600 R on the frequency spectra of the dislocation ultrasonic absorption Δd(f) in NaCl crystals in the frequency interval 37,5…232,5 MHz and at room temperature has been studied using the pulsed technique. From the frequency curves, taken from crystals with different doses of radiation, the dependencies of the viscosity coefficient B and the average effective length of the dislocation segment L from the dose of irradiation has been determined. The coefficient of dynamic viscosity B was found to be independent of the irradiation dose.

Iмпульсним методом в областi частот 37,5…232,5 МГц при T = 300 К дослiджено вплив попередньої деформацiї ε = 1,3% i опромiнення дозами 0…600 Р на хiд частотних спектрів дислокаційного поглинання ультразвуку Δd(f) в кристалах NaCl. З частотних кривих, знятих для кристалів із різними дозами опромінення, визначено залежності коефіцієнта в'язкості В і середньої ефективної довжини дислокаційного сегмента L від дози опромінення. Встановлено, що коефiцiєнт динамiчної в’язкостi В зi зростанням дози опромiнення залишається незмiнним.

Импульсным методом в области частот 37,5…232,5 МГц при T = 300 К исследованы влияния предварительной деформации ε = 1,3% и облучения дозами 0…600 Р на ход частотных спектров дислокационного поглощения ультразвука Δd(f) в кристаллах NaCl. Из частотных кривых, снятых для кристаллов с разными дозами облучения, определены зависимости коэффициента вязкости В и средней эффективной длины дислокационного сегмента L от дозы облучения. Установлено, что коэффициент динамической вязкости В с увеличением дозы облучения остается неизвестным.