Strength Improvement of Ferritic/Martensitic T91 Steel by Cross Wedge Rolling at Different Austenitizing Temperatures
Репозиторій DSpace/Manakin
- Домашня сторінка
- →
- Фізико-технічні та математичні науки
- →
- Відділення механіки
- →
- Проблемы прочности
- →
- Прoблемы прочности, 2017
- →
- Проблемы прочности, 2017, № 1
- →
- Переглянути статтю
JavaScript is disabled for your browser. Some features of this site may not work without it.
Strength Improvement of Ferritic/Martensitic T91 Steel by Cross Wedge Rolling at Different Austenitizing Temperatures
Інші назви:
Повышение прочности феррито-мартенситной стали Т91 после прокатки при различных температурах аустенизации
Тема:
Научно-технический раздел
УДК:
539.4
Посилання:
Strength Improvement of Ferritic/Martensitic T91 Steel by Cross Wedge Rolling at Different Austenitizing Temperatures / T. He, L. Min, H.J. Liu // Проблемы прочности. — 2017. — № 1. — С. 72-78. — Бібліогр.: 14 назв. — англ.
Підтримка:
This study has been perfomed within framework of the project ZKL-PR-200305 entitled “T91 Shaft Formed by Cross Wedge Rolling,” E3-0507-16-0201-16XKCZ01 entitled “Discipline Construction of Mechanical Engineering” and 16030501200 entitled “Research on Key Technologies of Underwater Vehicles for Deep-sea Oil and Gas Fields.” We wish to thank X. H. Zhang, M. Song, and L. B. Hang for discussions and advice, which resulted in significant improvements. The provision of microscopes at the Microscopy and Imaging Center at Texas A&M University is also gratefully acknowledged.
Remove selected
Дата:
2017
Переглядів:
343
Завантажень:
223
Анотація:
Cross wedge rolling (CWR) is a forming technique wherein the processed material microstructure is controlled by the processing temperature. The initial results on CWR-processed T91 steels at different austenitizing temperatures are discussed with the microstructure analysis by various characterization techniques, such as the optical and scanning electron microscopies. The processed T91 specimens were much harder than water-quenched ones, their hardness being independent of the ausforming temperatures despite their microstructural differences.