Nano-sized and micro-sized ZnWO₄ powders were obtained by different methods: hydrothermal synthesis with microwave heating, molten salt method, solid-state synthesis and сrushing of bulk crystals. Their morphological features were studied using transmission electron microscope and scanning electron microscope. The obtained nano- and micro-sized powders were used as fillers for flexible composite scintillators. The silicon rubber was used as a binder. The luminescent characteristics and scintillation performance of composite scintillators were measured. The dependence of scintillation performance of flexible scintillators on the morphological features of ZnWO₄ nanocrystallites was demonstrated. The flexible composite scintillator based on zinc tungstate obtained by solid-state synthesis with lithium nitrate addition was obtained and investigated. Its scintillation performance was close to that of a ZnWO₄ single crystal.
В настоящей работе проведены исследования, направленные на поиск эффективного способа получения порошка ZnWO₄ для разработки гибких композиционных сцинтилляторов с высокими функциональными характеристиками, такими как световой выход и уровень послесвечения.
У даній роботі проведені дослідження, спрямовані на пошук ефективного способу отримання порошку ZnWO₄ для розробки гнучких композиційних сцинтиляторів з високими функціональними характеристиками, такими як світловий вихід і рівень післясвітіння.