This study is an attempt of applying new electrolytes to obtain new generation oxide coatings. An oxide coating was deposited on aluminium Al(Al 99.5). The influence of an organic additive and anodizing parameters on the nanomorphology and nanostructure of the obtained coatings is described. The nanostructure and nanomorphology of oxide coatings were determined using a scanning electron microscope (SEM). An attempt was made to apply a new oxide coating for a sliding interaction with TGK 20/5 material. Tests were carried out under dry friction conditions. The friction coefficient was evaluated for the investigated sliding couple, as well as the intensity of wear of the specimens made of this material. The influence of the oxide coating nanostructure on the tribological properties of the tested couple was also determined.
Розроблено електроліти для формування нової генерації оксидних покривів на алюмінії. Методом сканівної електронної мікроскопії досліджено вплив органічних додатків до цих електролітів та параметрів анодування алюмінію на наноморфологію та наноструктуру покриву. Застосовано новий покрив у парі ковзання з матеріалом TGK 20/5. Випробувано за умов сухого тертя. Встановлено коефіцієнт тертя пари ковзання, а також інтенсивність зношування зразків з цього матеріалу. Визначено вплив наноструктури оксидного покриву на трибологічні властивості досліджуваної пари.
Разработаны электролиты для формирования новой генерации оксидных покрытий на алюминии. Методом сканирующей электронной микроскопии исследовано влияние органических добавок к этим электролитам и параметров анодирования алюминия на наноморфологию и наноструктуру покрытия. Применено новое покрытие в паре скольжения с материалом TGK 20/5. Испытано в условиях сухого трения. Установлен коэффициент трения пары скольжения, а также интенсивность изнашивания образцов из этого материала. Определено влияние наноструктуры оксидного покрытия на трибологические свойства исследуемой пары.