Electrophysical properties of PMN-PT-PS-PFN:Li ceramics

Abstract

We present the technology of obtaining and the electrophysical properties of a multicomponent material 0.61PMN-0.20PT-0.09PS-0.1PFN:Li (PMN-PT-PS-PFN:Li). The addition of PFN into PMN-PT decreases the temperature of final sintering which is very important during technological process (addition of Li decreases electric conductivity of PFN). Addition of PS i.e., PbSnO₃ (which is unstable in ceramic form) permits to shift the temperature of the maximum of dielectric permittivity. One-step method of obtaining ceramic samples from oxides and carbonates has been used. XRD, microstructure, scanning calorimetry measurements and the main dielectric, ferroelectric and electromechanical properties have been investigated for the obtained samples.

Ми представляємо технологiю отримання i електрофiзичнi властивостi багатокомпонентного матерiалу 0.61PMN-0.20PT-0.09PS-0.1PFN:Li (PMN-PT-PS-PFN:Li). Додавання PFN в PMN–PT понижує температуру кiнцевого спiкання, яка є дуже важливою пiдчас технологiчного процесу (додавання Li понижує електри-чну провiднiсть PFN). Додавання PS а саме, PbSnO₃ (який є нестiйким в керамiчному виглядi) дозволяє зсунути температуру максимуму дiелектричної сприйнятливостi. Використано однокроковий метод отримання керамiчних зразкiв з оксидiв i карбонатiв. Для отриманих зразкiв вивчено XRD, мiкроструктуру, проведено скануючi калометричнi вимiрювання i дослiджено головнi дiелектричнi, сегнетоелектричнi i електромеханiчнi властивостi.