Irradiation technique of constructional materials on the helium ions linac

Abstract

The irradiation technique of constructional materials on a helium ions LINAC is developed. Irradiations of metal, ceramic, and also semiconductor materials are carried out. During irradiation were measured: current of a ions beam, temperature of an exemplar and a slope angle of an exemplar to a beam axis. Also during experiments were controlled: an irradiation dose, profiles of a helium ion distribution and damage on exemplar thickness. Preliminary results show the considerable change of thermo-diffusion characteristics depending on beam energy and an irradiation dose. The phenomenological description of thermo-diffusion of the irradiated exemplars was offered.

Разработана методика облучения конструкционных материалов на линейном ускорителе ионов гелия. Проведены облучения металлических, керамических, а также полупроводниковых материалов. При облучении измерялись: ток пучка ионов, температура образца и угол наклона образца к оси пучка. Также в ходе экспериментов контролировались: доза облучения, профили залегания гелия и повреждения по толщине образца. Предварительные результаты показывают значительное изменение характеристик термодиффузии в зависимости от энергии пучка и дозы облучения. Предложено феноменологическое описание термодиффузии облучѐнных образцов

Розроблено методику опромінення конструкційних матеріалів на лінійному прискорювачі іонів гелію. Проведено опромінення металевих, керамічних, а також напівпровідникових матеріалів. Під час опромінення вимірювалися: струм пучка іонів, температура зразка і кут нахилу зразка до осі пучка. Також підчас експериментів контролювалися: доза опромінення, профілі залягання гелію і пошкодження по товщині зразка. Попередні результати показують значну зміну характеристик термодифузії в залежності від енергії пучка і дози опромінення. Запропоновано феноменологічний опис термодифузії опромінених зразків.