Effect of welding regime and filler content on structure of microalloyed Nb/Ti steel weldments

Abstract

In this paper changes in the proportions of certain microconstituents in the structure of weld metal and the heat affected zone are described and the mechanical and technological properties of welded joints of high-strength microalloyed Nb/Ti steel performed by E-process and MAG-process of welding with modification of the filler composition and welding parameters were analysed. The influence of different structures of filler material and welding parameters on the microstructure of HAZ and weld metal is studied with the aim to explain changes of mechanical and technological properties of welded microalloyed Nb/Ti steel joints.

Описано зміни в пропорціях між певними складниками мікроструктури металу зварного шва і зони термічного впливу; проаналізовано механічні та технологічні параметри зварних з’єднань високоміцної мікролегованої Nb/Ti сталі, виконаних за різних технологій зварювання з модифікацією складу наповнювача і параметрів зварювання. Вивчено вплив структури матеріалу наповнювача і параметрів зварювання на мікроструктуру зварних з’єднань для пояснення їх механічних і технологічних властивостей.

Описаны изменения в пропорциях между некоторыми составляющими микроструктуры металла сварного шва и зоны термического влияния; проанализированы механические и технологические параметры сварных соединений высокопрочной микролегированной Nb/Ti стали, выполненных в условиях разных технологий сварки с модификацией состава наполнителя и параметров сварки. Изучено влияние структуры материала наполнителя и параметров сварки на микроструктуру сварных соединений для объяснения их механических и технологических свойств.