Structure and strength properties of brazed joints of JS26NK cast nickel alloy. Part 2

Abstract

Materials science problems of formation of brazed joints in the JS26NK cast nickel alloy are considered. Physical-chemical properties of brazed joints, produced with application of standard boron-containing brazing alloy and brazing alloy containing silicon as second depressant, and different binders are presented. It is shown that application of a binder in the form of solution of acrylic acid in acetone is efficient in case of application of complex brazing alloys containing 20 % of the Ni--12 % Si (NS12) commercial brazing alloy powder. Achieved at room temperature strength and fracture toughness of a brazed joint from the JS26NK alloy exceed similar characteristics of the JS26VI alloy. Connection of mechanical properties of brazed joints with direction of dendrite growth in the metal being brazed is shown.

Рассмотрены материаловедческие особенности формирования паяных соединений в литейном никелевом сплаве ЖС26НК. Приведены физико-механические свойства паяных соединений, полученных с использованием стандартного бор- и кремнийсодержащего припоя и припоя, имеющего в качестве второго депрессанта кремний, а также различных связующих. Показано, что использование связующего в виде раствора акриловой кислоты в ацетоне является эффективным в случае применения комплексных припоев, содержащих 20 % порошка промышленного припоя Ni-12 % Si (НС12). Достигнутые при комнатной температуре прочность и вязкость разрушения паяного соединения из сплава ЖС26НК превышают аналогичные характеристики сплава ЖС26ВИ. Показана связь механических свойств паяных соединений с направлением преимущественного роста дендритов в паяемом металле.