Application of gamma activation analysis for research of Cs and I diffusion into a glassceramic matrix

Abstract

Nuclear reactions ¹³³Cs(γ,n)¹³²Cs, ¹²⁷I(γ,n)¹²⁶I were utilized for research of Cs and I diffusion in glassceramic matrices. The glassceramic matrix was manufactured with the help of hot isostatic pressing at 910°C and pressure 100 MPa. Diffusivities of cesium and iodine in a grain and through interphase boundary at 600°C were equal 10⁻¹¹ and 7.9⋅10⁻⁹ sm²/s, accordingly. The decrease of iodine diffusivity in a grain was observed at 750°C. A method of manufacture of glassceramic matrix for long-lived storage and nuclear-waste disposal ¹²⁹I is proposed.

Ядерные реакции ¹³³Cs(γ,n)¹³²Cs, ¹²⁷I(γ,n)¹²⁶I использовались для исследования диффузии Cs и I в стеклокерамической матрице. Стеклокерамическая матрица изготовлена при помощи газостатического прессования при 910°С и давлении 100 МПа. Коэффициенты диффузии цезия и йода в зерне и по границам зерен при 600°С составили 10⁻¹¹ и 7,9⋅10⁻⁹ см²/с, соответственно. Обнаружено уменьшение коэффициента диффузии йода в зерне при 750°С. Предложен способ создания матрицы для захоронения ¹²⁹I.

Ядерні реакції ¹³³Cs(γ,n)¹³²Cs, ¹²⁷I(γ,n)¹²⁶I використовувалися для дослідження дифузії Cs та I у склокерамічній матриці. Склокерамічна матриця виготовлена за допомогою газостатичного пресування при 910°С і тиску 100 МПа. Коефіцієнти дифузії цезію і йоду в зерні і по границях зерен при 600° С склали 10⁻¹¹ та 7,9⋅10⁻⁹ см²/с, відповідно. Виявлено зменшення коефіцієнта дифузії йоду в зерні при 750°С. Запропоновано спосіб створення матриці для поховання ¹²⁹I.