Nanostructured formations and coatings created on the surface of materials exposed to compression plasma flows

Abstract

The paper presents the results of investigations on changing silicon and aluminium morphology under the action of compression plasma flows generated by the quasi-stationary plasma accelerator (magnetoplasma compressor type). The feasibility of spraying nanostructured metal films by compression flows was demonstrated. The resulting single-layer coating consists of spherical particles measuring 50 to 200 nm. Such particles bonded to each other cover a surface relief including flat areas and regular structures developing during plasma action. The state and composition of a sample surface were studied by SEM- and EXD-methods

Представлено результати досліджень зміни морфології поверхні пластин кремнію й алюмінію при впливі на них компресійними плазмовими потоками, що генеруються квазістаціонарним плазмовим прискорювачем типу магнітоплазмовий компресор. Продемонстровано можливість нанесення на підкладки наноструктурних металевих покрить за допомогою компресійних потоків.

Представлены результаты исследований изменения морфологии поверхности пластин кремния и алюминия при воздействии на них компрессионными плазменными потоками, генерируемыми квазистационарным плазменным ускорителем типа магнитоплазменный компрессор. Продемонстрирована возможность нанесения на подложки наноструктурных металлических покрытий с помощью компрессионных потоков.