Effect of Molybdenum on Formation of Nanostructured Film at Friction of Titanium Material Ti—Cr—Mo—TiC

Abstract

The addition of molybdenum into the titanium material Ti—Cr—TiC significantly changes the composition and properties of nanostructured film, which is fabricated due to the friction on air and under high temperatures. Predominant contents of brittle oxide TiO2 (rutile) within the films in the process of friction determines the high wear of materials. There is no titanium oxide TiO2 within the newly fabricated film of titanium material containing molybdenum, whereas hydroxides and molybdenum oxides prevail in terms of quantity, and ensure high protective and lubricate properties of film.

Добавление молибдена в титановый материал Ti—Cr—TiC значительно изменяет состав и свойства наноструктурной плёнки, которая образуется в результате трения на воздухе при высоких температурах. Высокое содержание хрупкого оксида TiO2 (рутила) в плёнках в процессе трения определяет высокий износ материалов. Оксида TiO2 нет в свежеприготовленных плёнках титанового материала, содержащего молибден, в то время как гидроксиды и оксиды молибдена преобладают в количественном выражении и обеспечивают высокие защитные и смазочные свойства плёнки.

Додавання молібдену у титановий матеріял Ti—Cr—TiC значно змінює склад і властивості наноструктурної плівки, яка утворюється внаслідок тертя на повітрі за високих температур. Високий вміст крихкого оксиду TiO2 (рутилу) в плівках у процесі тертя визначає високий знос матеріялів. Оксиду TiO2 немає у щойноприготованих плівках титанового матеріялу, що містить молібден, у той час як гідроксиди й оксиди молібдену переважають у кількісній мірі і забезпечують високі захисні та змащувальні властивості плівки.