Crack growth in FeP04 steel under cyclic tension for different notches on the basis of its microstructure

dc.contributor.author	Rozumek, D.
dc.date.accessioned	2013-08-19T15:19:49Z
dc.date.available	2013-08-19T15:19:49Z
dc.date.issued	2008
dc.identifier.citation	Crack growth in FeP04 steel under cyclic tension for different notches on the basis of its microstructure / D. Rozumek // Проблемы прочности. — 2008. — № 1. — С. 121-124. — Бібліогр.: 7 назв. — англ.	uk_UA
dc.identifier.issn	0556-171X
dc.identifier.uri	http://dspace.nbuv.gov.ua/handle/123456789/48437
dc.description.abstract	We present the results of experimental work carried out in order to analyze the initiation and propagation of fatigue cracks in FeP04 steel. The tests were performed in plane specimens under cyclic tension by keeping constant the nominal load ratio R = 0. Crack paths on the basis of the tested material microstructure were observed.	uk_UA
dc.description.abstract	Представлены экспериментальные результаты анализа зарождения и распространения усталостных трещин в стали FеР04. Испытания выполнены на плоских образцах при циклическом растяжении и постоянном номинальном коэффициенте асимметрии цикла R = 0. Рассмотрены пути распространения трещин, исходя из микроструктуры материала.	uk_UA
dc.language.iso	en	uk_UA
dc.publisher	Інститут проблем міцності ім. Г.С. Писаренко НАН України	uk_UA
dc.relation.ispartof	Проблемы прочности
dc.subject	Научно-технический раздел	uk_UA
dc.title	Crack growth in FeP04 steel under cyclic tension for different notches on the basis of its microstructure	uk_UA
dc.title.alternative	Рост трещин в стали FeP04 при циклическом растяжении и различной форме	uk_UA