Modification of the surface of copper alloys with aluminum in the conditions of self-propagating high-temperature synthesis

Abstract

The influence of the technological parameters of the SHS process (temperature, holding time and alloying of B, Cr, Ti) on the corrosion resistance of brass with a surface alite layer, which effectively resists β-radiation, was studied. The research was carried out in 30% aqueous solutions of HNO₃, HCl, H₂SO₄. Aluminized coatings doped with silicon, which are obtained under optimal parameters, have 1.7-2.1 times higher corrosion resistance than doped B and Ti. Alloyed coatings have phases CuSi, CuAl, CuAl₂, CuTi, Ti₂Cu₃, CuCr, Cu₃Al, Cu₂Al, Al₃Si, and α-phase doped with Cr, Al, Si, B, Ti. When tested in a 30% aqueous solution of nitric acid, the coating doped with titanium and silicon shows a weight loss of 32 and 37 g/m², respectively.

Досліджено вплив технологічних параметрів СВС-процесу (температури, часу витримки та легування B, Cr, Ті) на корозійну стійкість латуні з поверхневим алітованим шаром, який ефективно протистоїть β-випромінюванню. Дослідження проводили в 30% водяних розчинах HNO₃, HCl, H₂SO₄. Алітовані покриття, леговані кремнієм, які отримані при оптимальних параметрах, мають у 1,7–2,1 рази вищу корозійну стійкість, ніж леговані B та Ti. Алітовані покриття мають фази: CuSi, CuAl, CuAl₂, CuTi, Ti₂Cu₃, CuCr, Cu₃Al, Cu₂Al, Al₃Si та α-фазу, леговану Cr, Al, Si, B, Ti. При випробуванні у 30% водному розчині HNO3 покриття, леговані титаном та кремнієм, мають втрату ваги відповідно 32 та 37 г/м².