Effect of iron on evolution of the structure of alloy Zr-1%Nb under ion irradiation

Abstract

This paper presents experimental data of the study of the influence of Fe alloying on the changes of the structure of the Zr-1%Nb alloy and evolution of the structure of this alloy under ion irradiation. It is shown that small additions of Fe to the Zr-1%Nb alloy lead to the change its structure due to the formation of Laves phase precipitates. Influence of ions Ar²⁺ irradiation on parameters of dislocation loops in alloy Zr1%Nb with Fe content 0.012…0.192 wt.% is studied by methods of transmission electron microscopy. Irradiations was carried out by Ar²⁺ ions (accelerator ESU-2) with energy 1.4 MeV, at temperature T = 390 °C. Dependence of density and size of dislocations on Fe content and on irradiation dose are obtained.

Представленo експериментальні дані дослідження впливу легування залізом на зміни структури та еволюції структури сплаву Zr-1%Nb під час іонного опромінення. Показано, що невеликі додавання Fe до сплаву Zr-1%Nb призводять до зміни його структури за рахунок утворення виділень фази Лавеса. Методами просвічуючої електронної мікроскопії досліджено вплив опромінення іонами Ar²⁺ на параметри дислокаційних петель у сплаві Zr-1%Nb з вмістом заліза 0,012…0,192 мас.%. Опромінення проводили іонами Ar²⁺ (прискорювач ЕСУ-2) з енергією 1,4 МеВ при температурі T = 390 °C. Отримано залежності щільності й розміру дислокацій від вмісту заліза і дози опромінення.