  • Correlation dependences between short-term/long-term static strength characteristics and creep resistance of tungsten at high temperatures 
    Borisenko, V.A.; Bukhanovskii, V.V.; Mamuzic, I. (Проблемы прочности, 2005)
    Experimental data on high-temperature mechanical properties under uniaxial tension of commercially pure tungsten obtained by powder metallurgy have been analyzed. It has been found that for powder metallurgy tungsten ...
  • Corrosion fatigue behavior of extruded AZ80, AZ61, and AM60 magnesium alloys in distilled water 
    Uematsu, Y.; Tokaji, K.; Ohashi, T. (Проблемы прочности, 2008)
    Rotary bending fatigue tests were conducted in laboratory air and distilled water using three extruded magnesium (Mg) alloys AZ80, AZ61, and AM60 with different chemical compositions. In laboratory air, thefatigue strengths ...
  • Corrosive and Mechanical Degradation of Pipelines in Acid Soils 
    Poberezhnyi, L.Ya.; Marushchak, P.O.; Sorochak, A.P.; Draganovska, D.; Hrytsanchuk, A.V.; Mishchuk, B.V. (Проблемы прочности, 2017)
    The effect of in-service degradation on the deformation behavior of the material of gas mains in soil acid electrolytes has been studied, and it has been shown that depending on the concentration of the corrosive components ...
  • Coupled Deformation and Diffusion Process at the Stainless Steel/Carbon Steel Interface in the Deformation Bonding Process 
    Li, S.; Zhang, Q.D.; Liu, J.Y. (Проблемы прочности, 2018)
    Cylindrical and surface-treated blanks were used to prepare stainless steel/carbon steel composite specimens at different temperatures. The coupled deformation and diffusion of materials at the interface were investigated ...
  • Coupled Effects of Strain Rate and Temperature on Deformation Twinning in Cu-Zn Alloy 
    Zhou, P.; Zhou, J.Q.; Ye, Z.X.; Jiang, E.; Hu, W.B.; Le, H.L. (Проблемы прочности, 2016)
    Cu-Zn alloy is an advanced material, but its deformation twinning mechanism still keeps unknown so far, especially the couple effects of temperature and strain rate. In this paper, a theoretical model of Cu-Zn alloy is ...
  • Crack growth in FeP04 steel under cyclic tension for different notches on the basis of its microstructure 
    Rozumek, D. (Проблемы прочности, 2008)
    We present the results of experimental work carried out in order to analyze the initiation and propagation of fatigue cracks in FeP04 steel. The tests were performed in plane specimens under cyclic tension by keeping ...
  • Crack Identification in Reinforced Concrete Beams Using ANSYS Software 
    Dahmani, L.; Khennane, A.; Kacia, S. (Проблемы прочности, 2010)
    Разработана трехмерная нелинейная конечноэлементная модель железобетонной балки. Для численного моделирования использовался стандартный конечноэлементный пакет программ ANSYS 8.0. С использованием объемных конечных ...
  • Crack initiation and endurance limit of hard steels under multiaxial cyclic loads 
    Bomas, H.; Kienzler, R.; Kunow, S.; Loewisch, G.; Schroeder, S. (Проблемы прочности, 2008)
    The endurance limit and the mechanisms o f fatigue crack initiation in the high cycle regime were investigated using round specimens o f the bearing steel 52100 under longitudinal forces and torsional moments and ...
  • Creep Failure Time of Thin-Walled Pipes under Combined Internal Pressure, Bending, and Tension 
    El Megharbel, A. (Проблемы прочности, 2010)
    Выполнен расчет долговечности в условиях ползучести для прямолинейных тонкостенных труб, подвергнутых совместному нагружению внутренним давлением, растягивающей силой и изгибающим моментом. Расчет времени до разрушения ...
  • Creep-Fatigue Behavior Evaluation by Reversible Permeability of CrMo Ferritic Steel for Ultra-Supercritical Steem Power Plants 
    Kim, C.S. (Проблемы прочности, 2016)
    The creep-fatigue of ferritic CrMo steel has been investigated by measuring the peak interval of the reversible magnetic permeability profile. The peak interval of reversible permeability was discussed in relation to the ...
  • Creep-induced structural changes in Ni-Si-B amorphous alloy 
    Jurikova, A.; Miskuf, J.; Csach, K.; Ocelik, V. (Проблемы прочности, 2008)
    The influence of the stress annealing on the reversible structural relaxation of a Ni-Si-B amorphous ribbon was studied. Creep-induced structural changes in the amorphous structure were derived from anisothermal DSC and ...
  • Creep Lifetime Assessment of Pressure-Tight PE100 Pipes Based on a Slow Fatigue Crack Growth 
    Luo, W.B.; Liu, Y.P.; Yin, B.Y.; Li, Y.; Liu, X. (Проблемы прочности, 2018)
    Polyethylene pipes are widely used in water supply, gas, and sewage systems due to their excellent mechanical properties. A slow crack growth is the primary fracture mechanism for the pipes under long-term internal pressures. ...
  • Cryogenic Fracture Behavior of Metastable Austenitic Stainless Steel in a High Magnetic Field 
    Shindo, Y.; Narita, F.; Suzuki, M.; Shindo, I. (Проблемы прочности, 2010)
    Исследуется влияние магнитного поля на закономерности разрушения метастабильной аустенитной нержавеющей стали при криогенных температурах. При испытании компактных образцов на растяжение в среде жидкого гелия при температуре ...
  • Cyclic cracking resistance of brittle materials in compressive loading 
    Lanin, A.G. (Проблемы прочности, 2009)
    Fatigue behavior of brittle materials under compression is considered. The findings should be taken into account in the failure probability assessment of components made of materials with limited plasticity, which are ...
  • Cyclic Inelasticity and High-Cycle Fatigue of Metals with Consideration of the Stress Gradient Effect 
    Troshchenko, V.T. (Проблемы прочности, 2011)
    Исследуется циклическое деформирование металлов и сплавов при многоцикловом циклическом нагружении в условиях неоднородного напряженного состояния. Показано существенное влияние градиента напряжений на циклическую неупругую ...
  • Cyclic Plastic Response and Damage in Materials for High Temperature Applications 
    Polák, J.; Obrtlík, K.; Petrenec M. (Проблемы прочности, 2014)
    In this contribution, the methods allowing to study the sources of cyclic stress and early fatigue damage at room and elevated temperatures are presented and used to reveal details of the mechanisms of cyclic plastic ...
  • Cовершенствование метода расчёта предела прочности горных пород при одноосном сжатии 
    Васильев, Д.Л. (Геотехническая механика, 2013)
    В основе метода расчёта положено дифференциальное уравнение предельного состояния с учётом внутреннего и контактного трения. В качестве закономерности распределения нормальных и касательных контактных напряжений использовано ...
  • Damage-Accounted Assessment of the Stress-Strain State of Structural Elements 
    Бобырь, Н.И.; Коваль, В.В. (Проблемы прочности, 2017)
    Приведены и проанализированы инженерные методы расчета напряжений и деформаций в зонах концентрации при упругопластическом деформировании конструктивных элементов. Показано, что для оценки кинетики эффективных коэффициентов ...
  • Damage and Fracture of VT22 Titanium Alloy in Static Tension after the Application of Additional Pulse Loading 
    Марущак, П.О.; Коноваленко, І.В.; Чаусов, М.Г.; Пилипенко, А.П. (Проблемы прочности, 2017)
    Установлено основні закономірності пластичного деформування титанового сплаву ВТ22 та мікромеханізми його руйнування за статичного розтягу та розтягу після різних режимів динамічного нерівноважного навантаження в результаті ...
  • Deep-Drawing Process Simulation for Tailor-Welded Blanks with an Elastic Blankholder 
    Brusilová, A.; Schrek, A.; Švec, P.; Gábrišová, Z. (Проблемы прочности, 2017)
    Application of tailor welded blanks is proved to be very effective in the current trend of body parts construction. However, their formability is limited to the differences of mechanical properties of individual tailor ...