Experimental and Numerical Analysis of Springback Behavior of Aluminum Alloys

Abstract

Presented work deals with springback behavior of two different aluminum alloys, one falling into 5th series (AW-5754 H22) with a thickness of 0.8 mm and other from 6th series (AW-6082 T6) with 1.0 mm thickness. These materials are used for their various applications and hardening process. The springback behavior was investigated by U-bending test. Bending tool was graduated jig with rollers and experiment was performed on R11 and R17 radii. The first series of specimens were oriented in a parallel direction and the other in a direction perpendicular to the rolling direction. Experimental results were measured with MATLAB measuring method and compared with finite element calculation carried out in PAM-STAMP. Influence of different yield functions was also examined.

Рассматривается характеристика упругой отдачи двух различных алюминиевых сплавов: AW-5754 H22 толщиной 0,8 мм, принадлежащего к 5-й серии, и AW-6082 T6 толщиной 1,0 мм, принадлежащего к 6-й серии. Эти материалы используются для разнообразного применения, включая процесс упрочнения. Характеристика упругой отдачи исследовалась при испытаниях на U-образный изгиб. В качестве гибочного инструмента использовалось приспособление с роликами, и эксперимент проводился на радиусах R11 и R17. Одна группа образцов была ориентирована в направлении, параллельном направлению прокатки, другая в перпендикулярном. Экспериментальные результаты, полученные с использованием программного комплекса MAТLAB, сравнивались с расчетом методом конечных элементов с помощью программы PAM-STAMP. Исследовалось также влияние различных функций текучести.