Effect of Aging Treatment on Surface Roughness, Mechanical Properties, and Fracture Behavior of 6xxx and 7xxx Aluminum Alloys

Abstract

The effect of aging treatment on the surface roughness and mechanical properties of AA6061 and AA7075 alloys was studied. Microhardness and tensile tests were used to investigae the mechanical properties. X-ray diffraction analysis was used to investigate the surface of the specimens. Furthermore, after tensile tests fractured surfaces were examined with scanning electron microscopy. An atomic force microscope was employed for analysis of the effect of aging treatment on surface roughness. Higher surface roughness with an increase in the volume fraction of the precipitate was revealed.

Исследовано влияние процесса старения на шероховатость поверхности и механические свойства алюминиевых сплавов AA6061 и AA7075. Механические свойства исследовали при испытаниях на микротвердость и растяжение. Поверхность образцов исследовали с помощью рентгеноструктурного анализа. После испытания на растяжение поверхность разрушения исследовали методом растровой электронной микроскопии. Влияние процесса старения на шероховатость поверхности изучали с помощью атомно-силового микроскопа. Показано, что с ростом шероховатости поверхности увеличивается количество выделившихся фаз.

Досліджено вплив процесу старіння на шорсткість поверхні і механічні властивості алюмінієвих сплавів АА6061 та АА7075. Механічні властивості досліджували при випробуваннях на мікротвердість і розтяг. Поверхню зразків досліджували за допомогою рентгеноструктурного аналізу. Після випробувань на розтяг поверхню руйнування досліджували методом растрової електронної мікроскопії. Вплив процесу старіння на шорсткість поверхні вивчали за допомогою атомно-силового мікроскопа. Показано, що з ростом шорсткості поверхні збільшується кількість виділених фаз