Structure, Phase Composition of Supercooled Austenite, and Kinetics of Its Decomposition in Perlite Temperature Range of Chromium–Manganese Cast Iron

Abstract

The current paper studies the kinetics features of supercooled austenite decomposition in the pearlite temperature range (600–500°C) in chromium–manganese cast iron with the content of 2.2% carbon, 12.63% chromium, 5.7% manganese. The structure formation, phase composition, hardness as well as the distribution of elements between the phases and the structural constituents of the above-mentioned cast iron after isothermal soaking are investigated. The average size of secondary carbides after isothermal soaking is determined using JMicroVision v.1.2.7 free software.

В работе рассмотрены особенности кинетики распада переохлаждённого аустенита в перлитной области температур (600–500°C) в хромомарганцевом чугуне с содержанием 2,2% углерода, 12,63% хрома и 5,7% марганца. Изучено структурообразование, фазовый состав, твёрдость, а также распределение элементов между фазами и структурными составляющими исследуемого чугуна после изотермических выдержек. C помощью бесплатного программного обеспечения JMicroVision v.1.2.7. определён средний диаметр вторичных карбидов после изотермических выдержек.

У роботі розглянуто особливості кінетики розпаду переохолодженого аустеніту в перлітній області температур (600–500°C) у хромоманґановому чавуні, що містить 2,2% вуглецю, 12,63% хрому та 5,7% манґану. Вивчено структуроутворення, фазовий склад, твердість, а також розподіл елементів між фазами та структурними складовими чавуну, який досліджувався після ізотермічних витримок. За допомогою безкоштовного програмного забезпечення JMicroVision v.1.2.7. визначено середній діяметер вторинних карбідів після ізотермічних витримок.