  • Nikitin, A.V.; Tolstolutskaya, G.D.; Ruzhytskiy, V.V.; Kopanets, I.E.; Karpov, S.A.; Vasilenko, R.L.; Rostova, G.Y.; Rybalchenko, N.D.; Sungurov, B.S. (Вопросы атомной науки и техники, 2017)
    Processes of blisters and associated subsurface cracks nucleation during exposure of 12Cr2MoNbVB ferritic-martensitic steel and α-Fe under glow discharge hydrogen (deuterium) plasma with ion energies of ~ 1 keV and ion ...
  • Tolmachova, G.N.; Tolstolutskaya, G.D.; Karpov, S.A.; Sungurov, B.S.; Vasilenko, R.L. (Вопросы атомной науки и техники, 2015)
    The possibility of application of nanoindentation technique for investigation of mechanical properties (hardness and modulus of elasticity) of SS316 steel irradiated with 1.4 MeV Ar⁺ ions to a dose of 1·10¹⁷ cm⁻² at 900 K ...
  • Tolstolutskaya, G.D.; Kuprin, A.S.; Voyevodin, V.N.; Nikitin, A.V.; Ovcharenko, V.D.; Belous, V.A.; Vasilenko, R.L.; Kopanets, I.E. (Вопросы атомной науки и техники, 2017)
    The surface topography and deuterium retention in W, Ta and W-Ta coatings under the influence of low-energy deuterium plasma was studied. It was observed formation of blisters as dome and burst or delaminated structures. ...
  • Nikitin, A.V.; Kuprin, A.S.; Tolstolutskaya, G.D.; Vasilenko, R.L.; Ovcharenko, V.D.; Voyevodin, V.N. (Вопросы атомной науки и техники, 2018)
    The surface topography of W bulk prepared by powder sintering (20 μm thickness) and W coatings deposited by cathodic arc evaporation and by argon ion sputtering was studied under the influence of low-energy hydrogen (deuterium) ...
  • Tolstolutskaya, G.D.; Rostova, G.Y.; Voyevodin, V.N.; Velikodnyi, A.N.; Tikhonovsky, M.A.; Tolmachova, G.N.; Kalchenko, A.S.; Vasilenko, R.L.; Kopanets, I.E. (Вопросы атомной науки и техники, 2017)
    Nanoindentation was used to measure the ion irradiation effect on hardening of Cr-Fe-Ni-Mn high-entropy alloys with different composition. Alloys were irradiated with 1.4 MeV Ar ions at room temperatures and midrange doses ...
  • Belous, V.A.; Borodin, O.V.; Bryk, V.V.; Vasilenko, R.L.; Voyevodin, V.N.; Kuprin, A.S.; Ovcharenko, V.D.; Reshetnyak, E.N.; Tolmachova, G.N. (Functional Materials, 2013)
    In this work we studied structure of Ti—20Zr alloy in recrystallized and nanocrystalline conditions before and after irradiation by Zr³⁺ ions with energy 1.8 MeV to 80 dpa at 500° C. By transmission electron microscopy ...
  • Lunyov, V.M.; Kuprin, A.S.; Ovcharenko, V.D.; Belous, V.A.; Morozov, A.N.; Ilchenko, A.V.; Tolmachova, G.N.; Reshetnyak, E.N.; Vasilenko, R.L. (Вопросы атомной науки и техники, 2016)
    W, Ta and W-Ta coatings were deposited by argon ion sputtering of targets made from appropriate metals using the gas plasma source. Mechanical properties of the obtained coatings were investigated by the methods of X-ray ...
  • Nikitin, A.V.; Tolstolutskaya, C.D.; Ruzhytskiy, V.V.; Kopanets, I.E.; Karpov, S.A.; Vasilenko, R.L.; Rostova, G.Y.; Rybalchenko, N.D. (Вопросы атомной науки и техники, 2016)
    Surface topography and deuterium interaction with a-Fe under glow discharge hydrogen (deuterium) ions bombardment with energy of ~1 keV at ion fluencies of (0.02…1)∙10²⁴ D/m² and various temperatures have been examined. ...
  • Kopanetz, I.E.; Tolstolutskaya, G.D.; Nikitin, A.V.; Bilous, V.A.; Kuprin, A.S.; Ovcharenko, V.D.; Vasilenko, R.L. (Вопросы атомной науки и техники, 2015)
    Depth distribution profiles of deuterium in zirconium alloy Zr-1Nb in initial state and with coatings Cr, CrN, and Cr₂O₃ after ion implantation with 15 keV/D⁺ at temperatures 350 °C to dose 1·10¹⁷ D/cm⁻² and deuterium ...